Products

Nylon sheet

Product details

1. Nylon Sheet
A polyamide is a macromolecule with repeating units linked by amide bonds. Polyamides occur both naturally and artificially. Examples of naturally occurring polyamides are proteins, such as wool and silk. Artificially made polyamides can be made through step-growth polymerization or solid-phase synthesis yielding materials such as nylons, aramids, and sodium poly (aspartate). Synthetic polyamides are commonly used in textiles, automotive applications, carpets and sportswear due to their high durability and strength. The transportation industry is the major consumer, accounting for 35% of polyamide (PA) consumption.
 
2 Specification

Thickness Standard size Custom size/shape
5-250mm
 
1220*2440mm;1000*3000mm
2000*4000mm;1500*7000mm
On demand

3. Colors Available
Black, White, Red, Yellow, Blue, Green, Orange etc according to pantone and Ral color number.
 
4.Material Datasheet

Item PA6 PA66 PA610 PA612 PA9 PA11 PA12 PA1010
Density (g/cm3) 1.13 1.15 1.07 1.07 1.05 1.04 1.02 1.07
Melting point (℃) 215 252 220   185 186 178 210
Thermal deformation temperature (℃) 68 75 82     54 55  
Coldness resistance temp.(℃) -30 -30 -40   -30 -40   -40
Tensile strength (mpa) 75.0 80.0 60.0 62.0 65.0 56.0 65.0 55.0
Compression strength (mpa) 85.0 105.0     72.5 70.0   65.0
Bending strength (mpa) 120.0 60~100 90.0   85.0 70.0 90.0 80.0
Notch impact strength (kj/m2) 5.5 5.4 5.5     3.86   5
Volume resistivity (ω* cm) 10^12 10^14 10^14 10^12 10^14 10^13 10^14 10^15
Dielectric constant (1mhz) 3.4 3.6 3.5 3.5 3.7 3.7 3.1 3.1
Dielectric loss (1mpz) 0.03 0.03 0.04 0.02 0.018 0.04 0.03 0.026
Dielectric strength (kj/mm) 16 16 16 16 16 17 18 15
Molding shrinkage(%) 0.8~2.5 1.5~2.2 1.5~2   1.5~2.5 1.2   1~2.5